Flame-retardant UHMWPE plates flame resistance plastic panles

Abson uhmwpe panles data sheet:

*Density: 0.92--0.96g/cm3

*Tensile strength at yield: 15--20Mpa

*Notched impact strength: 80--170 KJ/M2

*Abrasion resistance(sand slurry test): 70--120%

*Shore hardness D : 63--68o

*Max.cont.temperature: 80℃

Inquire Now

PRODUCTS DESCRIPTION

Flame-retardant UHMWPE plates/flame resistance plastic panles

Ultrahigh-molecular-weight polyethylene (UHMWPE) is defined by ASTM as “polyethylene with molecular weight over three million (weight average). Our UHMWPE products have molecular weight range from 1 ~ 9 million. Being chemically similar to UHMWPE shows the typical polyethylene characteristics of chemical inertness, lubricity, and electrical resistance, while its very long substantially linear chains provide greater impact strength, abrasion resistance, toughness, and freedom from stress cracking.However, this very high molecular weight also makes it difficult to process the polymer by standard moulding techniques. Compression molding of sheets and ram extrusion of profiles are the normal manufacturing techniques.

Characters:

1.Very low dynamic friction coefficient(15)

2.Extreme wear resistance (200%higher than stainless steel)

3.Resistance to chemicals

4.Corrosion resistance.

5.High impact strength(upto 170KJ/M2)

6.Service temperature range-260℃ to +80℃